Portfolio Brief
Refractory Cement/Binder
The Refractory Cements within our product range are distinguished by their exceptional quality and durability. It is produced through the grinding of aluminate cement clinker. Refractory cement is a newly developed material characterized by its exceptional heat-resistant properties, and it is extensively utilized in industrial applications.
It is extensively utilized in high-temperature industries as a premium additive material or adhesive. Additionally, it serves as a refractory binders.
Technical Specification
High Alumina Refractory Cement
AIL HARC-50
AIL HARC-70
AIL HARC-75
Chemical Properties
Chemical Properties
Al2O3
AIL HARC-50
47-50 %
AIL HARC-70
68-70%
AIL HARC-75
73-75 %
Chemical Properties
Fe2O3
AIL HARC-50
6.0-8.0 %
AIL HARC-70
0.1-0.5 %
AIL HARC-75
0.1-0.5 %
Chemical Properties
CaO
AIL HARC-50
30-34%
AIL HARC-70
28-31 %
AIL HARC-75
23-28 %
Physical & Thermal Properties
Setting Time (Minutes)
Setting Time (Minutes)
Initial
AIL HARC-50
20 to 70
AIL HARC-70
50 to 120
AIL HARC-75
60 to 120
Setting Time (Minutes)
Final
AIL HARC-50
300 to 390
AIL HARC-70
400 to 490
AIL HARC-75
450 to 550
Physical & Thermal Properties
Specific Surface Area (cm2/g)
AIL HARC-50
2800-3600
AIL HARC-70
3500-4200
AIL HARC-75
3500-4200
Cold Crushing Strength (kg/cm2):
Cold Crushing Strength (kg/cm2):
After 1 Day
AIL HARC-50
300-370
AIL HARC-70
400-500
AIL HARC-75
350-450
Cold Crushing Strength (kg/cm2):
After 1 Day Curing + Drying at 1100C/24h
AIL HARC-50
-
AIL HARC-70
520-650
AIL HARC-75
500-650
Cold Crushing Strength (kg/cm2):
After 3 Days
AIL HARC-50
400-480
AIL HARC-70
-
AIL HARC-75
-
Physical & Thermal Properties
Refractoriness (0C/OC) min.
AIL HARC-50
1337/12
AIL HARC-70
1564/20
AIL HARC-75
1683/31
Packaging: 25 kg bags
Delivery State: Dry
Storage Life: Best till 9 months from the date of production, if stored in proper condition.
Note: The data are current production averages. They can not be used as limits for specification
Features
- Higher Temperature Resistance
- Higher Thermodynamic Stability
- Higher Compressive Strength
- Higher Tensile Strength
- Good Structural Integrity
- Lower Impurity Content
- Excellent Bonding Properties
Application
- Refractory Manufacturing
- Construction Industry
- Engineering
- Steel Industry
- Power Plants
- Petrochemical Industry
- Cement Industry